Si-SiC composite foams were prepared using tannin-based foams as templates. The foams were prepared by four different methods for the determination of which method would best produce a foam with a pore size under 200 µm. The foam samples were characterized by SEM, XRD, and Raman spectroscopy, and the thermal conductivity of one of the foams was investigated by the transient plane source method. It was found that direct infiltration of ...
Carbon/liquid-crystal polymer composites were formulated. Composites containing one of three types of carbon filler, composites containing two types of carbon filler, and composites containing all three types of carbon filler were prepared to test not only the effect of each filler on the thermal conductivity of the composite, but also the effect of combining fillers. The anisotropic method on a TPS system was used for the thermal conductivity measurements. ...
Composite carbon foams were prepared by mixing tannin-based resin with various graphite powders in an effort to improve the thermal conductivity relative to pristine carbon foams in order to use them as hosts for phase-change materials. It was found that using graphite powder with smaller particle sizes resulted in foams with a higher bulk density than those prepared with an equal amount of larger graphite particles, this increased density resulted ...
The authors have investigated the use of silver nanomaterials as a filler in epoxy resin in an effort to identify a composite resin with a high thermal conductivity for application as a thermal interface material. It was determined that the addition of silver nanoparticle and silver nanowires both increased the thermal conductivity of the resin, but the silver nanowires caused a much more drastic increase. It was found that by ...
The authors present a method of preparing an aluminum shoe mold by a novel process called vacuum sealed casting. It was determined that the prototype shoe should be made of a resin, and then the mold should be made of aluminum. A composite resin was chosen such that the thermal conductivity, dimension accuracy, and wear resistance were greater than those of the pristine resin. The use of the aluminum mold ...