Keywords: alumina porcelain, bulk density, ceramics, differential thermal analysis, differential thermal analysis (dta), dta, specific heat, tga, thermal conductivity, thermal diffusivity, thermodilatometry, thermogravimetric analysis, thermogravimetric analysis (tga), tps method, transient plane source, transient plane source (tps) method
Abstract: The thermal properties, as well as bulk density, and mass loss of alumina porcelain were determined as a function of firing temperature. It was found that after sintering at 1320 ºC, the thermal conductivity and thermal diffusivity increased by ~700% and ~400%, respectively.
Reference: Ceramics International 41, 2B (2015) 3254-3258
DOI: 10.1016/j.ceramint.2014.11.015