Poly(trimethylene terephthalate)-block-poly(tetramethylene oxide) (PTT-PMTO) copolymer-based nanocomposites containing a combination of single-walled carbon nanotubes (SWCNTs) and graphene nanoplatelets (GNPs) as carbon nanofillers were investigated to determine their thermal conductivities. Nanocomposites having a total carbon nanofiller concentration of 0.4 and 0.6 wt. % were preparared with varying amounts of each nanofiller, and the thermal conductivity was measured using the transient plane source (TPS) method. The dispersion of the nanofillers was observed by ...
The thermal conductivities of four composite paraffin phase change materials (PCMs) containing embedded multi-walled carbon nanotubes (MWCNTs) with varying dimensions were determined. The goals of this study were to investigate the interfacial thermal resistance between two MWCNTs, and to investigate the ballistic and diffusive components of the thermal resistance at the interface. It was found that the thermal conductivity of the composite PCMs increased with the diameter of the MWCNT ...
The effects of silver nanowire size on the thermal conductivities of ethylene glycol-based nanofluids were investigated experimentally. The effects of altering the loading concentration of nanowires, and altering the temperature were also investigated. In addition to this, an investigation into the effects of the nanowire dimensions on the rheological properties of the nanofluids was also conducted. Theoretical models were then developed based on the experimental results....
The potential of graphene and few-layer graphene to be used as fillers in a paraffin wax phase change material (PCM) was evaluated. The goal was to prepare a composite PCM with a higher thermal conductivity than the pure paraffin wax. The ability of the composite PCM to reduce temperature variation in lithium ion batteries was also evaluated over 10 charging – discharging cycles. It was found that ...
The effective thermal conductivity and thermal diffusivity was measured for chalcogenide glass samples of the formulation Ge30-xSe70Sbx (x = 10, 15, 20, 25). It was found that both the effective thermal conductivity and thermal diffusivity were independent of temperature up to 160º C. After this point, both properties were found to increase with increasing temperature until they reached a maximum value at a point near the glass transition temperature of the glass. After reaching ...