The influence of In content in the Se98-xAg2Inx (x = 0, 2, 4, 6) system of chalcogenide glasses on the physical properties of the glasses were investigated by the authors. The maximum thermal conductivity and thermal diffusivity value was observed for the sample containing 2 at. % In. The microhardness was found to initially decrease upon doping of In for Se; however, it began to slowly increase after a certain In content had been attained. ...
CdS nanoparticles were dispersed in varying quantities into a PVC matrix and the effective thermal conductivities of the produced nanocomposites were investigated at temperatures from 25 to 110C. It was determined that the dispersion of the nanoparticles in PVC caused an increase in thermal conductivity up to 2 wt. % filler concentration when compared to that of pure PVC. When more than 2 wt. % of filler was added to the PVC matrix, the thermal ...
The thermoelectric properties of the Ca1-xGdxMnO3-delta system where x= 0.00, 0.02, and 0.05 were evaluated. It was determined that the sample with the lowest electrical resistivity was the Ca0.95Gd0.05MnO3-delta sample. This result was attributed to the increase content of Mn3+ in the Mn4+ matrix resulting from doping of gadolinium. The dominant charge carriers in all samples were holes, as the thermopower was negative. The highest thermoelectric figure of ...
Bi2-xSbxTe3 thermoelectric materials, where x = 1.52 and 1.55 were prepared and evaluated for their thermoelectric properties. Three samples in total were prepared, two with x = 1.52 and 1.55 were synthesized at 140oC and one with x = 1.55 was synthesized at 160 oC. It was determined that the two samples synthesized at the higher temperature had lower resistivity than that which was synthesized at higher temperature. The figure of merit for the sample synthesized at 140oC, ...
The partial replacement of Ca2+ ions with Eu3+ in the Ca3Co3.95Ga0.05O9+delta system to give polycrystalline samples of Ca3-xEuxCo3.95Ga0.05O9+delta (x = 0.00, 0.02, and 0.10) was performed in order to assess the effect that the dopant had on thermoelectric properties of this system. It was found that the electrical resistivity and thermopower increased with increasing Eu3+ content, and the thermal conductivity decreased. The highest thermoelectric figure of ...