The partial replacement of Ca2+ ions with Eu3+ in the Ca3Co3.95Ga0.05O9+delta system to give polycrystalline samples of Ca3-xEuxCo3.95Ga0.05O9+delta (x = 0.00, 0.02, and 0.10) was performed in order to assess the effect that the dopant had on thermoelectric properties of this system. It was found that the electrical resistivity and thermopower increased with increasing Eu3+ content, and the thermal conductivity decreased. The highest thermoelectric figure of ...
The partial replacement of Ca2+ ions with Eu3+ in the Ca3Co3.95Ga0.05O9+delta system to give polycrystalline samples of Ca3-xEuxCo4O9+delta (x = 0.00, 0.05, and 0.10) was performed in order to assess the effect that the dopant had on thermoelectric properties of this system. It was found that the electrical resistivity and thermopower increased when Eu3+ is added, and the thermal conductivity decreased. The highest thermoelectric figure of merit ...
A paraffin-based composite phase change material (PCM) was prepared by the addition of hexagonal boron nitride (h-BN) nanosheets to melted paraffin wax followed by vigorous stirring. The nanosheets were added in quantities ranging from 1 to 10 wt. %. A reference sample of pure paraffin was also prepared. It was determined that the addition of h-BN nanosheets resulted in an increase in thermal conductivity and that the melting and solidification rates were also ...
La0.7Ba0.15Sr0.15MnO3 (LBSMO) powder was prepared and mixed with HDPE powder in volume fractions from 0 to 0.30. These powders were then molded into pellet form in a hot press and cooled to room temperature. The thermal conductivity of the resulting composite was then measured using the transient plane source method. It was found that the thermal conductivity of the composite samples increased with increasing LBSMO content up to an ...
A composite PCM was prepared from n-octadecane and mesoporous silica (MPSiO2) nanoparticles. The nanoparticles were added in quantities ranging from 1 wt. % to 5 wt. %, and the thermal conductivity of each composite sample was determined as a function of temperature. The most significant enhancement in thermal conductivity was observed in the sample containing 3 wt. % MPSiO2 nanoparticles. The viscosity of the composite samples was also investigated and it was found that at mass ...