The authors present a method of preparation of TiO2 nanotubes by alkaline treatment (with NaOH) of TiO2 particles followed by acid-washing and annealing treatment. Theoretical and experimental studies on the thermal conductivity of TiO2 nanotubes is also presented. The thermal conductivity values determined experimentally matched well with theoretical values obtained. It was found that TiO2 nanotubes had a lower thermal conductivity than the original TiO2 particles. This phenomenon was attributed ...
Thermal interface resistance results from small gaps and surface geometry mismatches between two materials that make up a composite. Thermal interface resistance is present in most any material that is comprised of two or more components. In the field of thermal interface materials, the majority of novel materials are composites, and thus are subject to thermal interface resistance and thermal boundary resistance (thermal discontinuity at a perfectly bonded interface of ...
Using industrial grade mullite powder and a foaming and starch consolidation process, a series of porous mullite ceramics were prepared. These ceramics were analyzed by a thermal constants analyzer, and it was determined that the ceramics had low thermal conductivities and would make good thermal insulators. The porosity of the synthesized ceramics can be controlled by the sintering temperature and by adjusting solid loading. The ceramics were subjected to theoretical ...