La0.7Ba0.15Sr0.15MnO3 (LBSMO) powder was prepared and mixed with HDPE powder in volume fractions from 0 to 0.30. These powders were then molded into pellet form in a hot press and cooled to room temperature. The thermal conductivity of the resulting composite was then measured using the transient plane source method. It was found that the thermal conductivity of the composite samples increased with increasing LBSMO content up to an ...
The thermoelectric and magnetic properties of the Ca3Co4-xCuxO9+delta system where x = 0, 0.05, 0.07, 0.10, and 0.15 were investigated as materials of this type have potential for use in thermoelectric generators. The goal of this work was to identify the sample in this system having the highest thermoelectric figure of merit. To accomplish this, a high thermopower, a high thermal voltage, a low resistivity, and a low thermal conductivity were required. It ...
A disc of a composite ceramic material composed of silicon nitride (Si3N4) and 20% hBN was prepared and its tribological characteristics were investigated by sliding a Si3N4 pin across its surface at different sliding speeds. The friction coefficient and wear coefficient were determined for the composite using two different test modes: one in which the pin was kept stationary and the disc was rotated on top of the pin, ...
Lutetium aluminum garnet activated by cerium (LuAG:Ce) materials containing functional materials (SiO2 and MgO) were prepared. These materials are used in LEDs, and they require a high thermal conductivity in order to minimize thermal aging. The functional materials were added in order to increase the thermal conductivity, as well as the luminescent properties of these materials. It was found that SiO2 did not improve the luminescent properties, but MgO ...
The thermal and mechanical properties of concrete in which normal weight aggregate has been substituted with lightweight aggregates were investigated. The properties were found to be dependent on the volume fraction of the lightweight aggregate, as well as on the nature and quality of the aggregate. The addition of lightweight aggregates resulted in a decreased thermal conductivity, as well as a decreased thermal diffusivity in all samples. The compressive strength ...