A series of Bi(2-x)Sb(x)Te3 powders were prepared via hydrothermal methods by varying x (x=1.45, 1.50, 1.55, 1.56). These powders were then heavily characterized by XRD, EDS, ICP-AES, TEM, SEM and the TPS technique. A low thermal conductivity was desired, so as to give the highest thermoelectric figure of merit (ZT). It was determined that the highest figure of merit was obtained when x=1.55, which resulted in a value of 1.65 ...