The thermoelectric properties of two thermoelectric materials (Ca3Co4O9+delta and Ca3−xPrxCo3.95Ga0.05O9+delta) were investigated in this paper. The power factor of one of the samples was improved by 52% relative to the others. The second material tested had a 50% improvement in the figure of merit over the first material. The study concluded that partial substition of the Pr3+ ions can improve the thermoelectric properties of these ...
The low-temperature thermoelectric properties of Ca3-xDyxCo4O9+delta systems (x = 0, 0.02, 0.05, and 0.10). It was determined that these systems produced positive thermopower, indicating that the dominant carriers were holes. The electrical resistivity and thermal conductivity were found to decrease with increasing Dy3+ content, and the thermopower was found to increase. The highest calculated thermoelectric figure of merit was 0.044, and this was calculated for the Ca2.9Dy0.1Co4O9+delta sample....